流體輸送用Q345B無縫鋼管的尺寸允許偏差
|
熱軋(擠、擴)鋼管 |
冷拔(軋)鋼管 |
|
|
尺寸／mm |
允許偏差／mm |
尺寸／mm |
允許偏差／mm |
|
|
普通級 |
較高級 |
普通級 |
較高級 |
|
|
外徑D |
68≤D≤159 |
±1.25 |
±1 |
外徑D |
6-10 |
±0.20 |
±0.15 |
|
|
>10-30 |
±0.30 |
±0.20 |
|
|
159 |
±1.5 |
>30-50 |
±0.40 |
±0.30 |
|
|
>50 |
±0.9％ |
±0.8％ |
|
|
壁厚S |
>15 |
+15
-12.5 |
±12.5 |
壁厚S |
0.5-1 |
±0.15
±14％ |
±0.12 |
|
|
>1-3 |
|
+12％
-10％ |
|
|
≥15 |
+20
-15 |
|
|
>3 |
+12％
-10％ |
±10％ |
|
注：鋼管的彎曲度不得大于如下規(guī)定:
壁厚<15mm……………………………………………………1.5mm／m
壁厚≥15mm……………………………………………………2.0mm／m
熱擴管…………………………………………………………3.0mm／m
(1) 牌號和化學成分
|
組織
類型 |
序號 |
牌 號 |
化學成分(質(zhì)量分數(shù))(％) |
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Ti |
其他 |
|
奧氏
體型 |
1 |
0Cr18Ni9 |
≤0.07 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-11.00 |
17.00-19.00 |
|
|
|
|
2 |
00Crl9Ni10 |
≤0.03c |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-12.00 |
18.00-20.00 |
|
|
|
|
3 |
0Cr23Ni13 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.0-15.00 |
22.0-24.00 |
|
|
|
|
4 |
0Cr25Ni20 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
19.00-22.00 |
24.00-26.00 |
|
5wc-0.07 |
|
|
5 |
0Crl8Ni10Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
9.00-12.00 |
17.00-19.00 |
|
≥5wc |
|
|
6 |
0Crl8Ni11Nb |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
9.00-13.00 |
17.00-19.00 |
|
|
Nb≥10wc |
|
7 |
0Crl7Nil2Mo2 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.00-14.00 |
16.00-18.50 |
2.00-3.00 |
|
|
|
8 |
00Crl7Ni14Mo2 |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00-15.00 |
16.0-18.00 |
2.00-3.00 |
|
|
|
9 |
0Crl9Nil3Mo3 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-15.00 |
18.00-20.00 |
3.00-4.00 |
|
|
|
10 |
00Crl9Nil3Mo3 |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-15.00 |
18.00-20.00 |
3.00-4.00 |
|
|
|
11 |
0Crl8Nil2Mo2Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
1.80-2.50 |
5wc-0.70 |
|
|
12 |
1Crl8Nil2Mo2Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
1.80-2.50 |
5(wc-0.02)
-0.80 |
|
|
13 |
0Crl8Ni12Mo3Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
2.50-3.50 |
5wc-0.70 |
|
|
14 |
lCrl8Ni12Mo3Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
1.00-14.00 |
16.0-19.00 |
2.50-3.50 |
5(wc-0.02)
-0.80 |
|
|
15 |
0Cr18Ni12Mo2C |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
17.00-19.00 |
1.20-2.75 |
|
Gul.0-2.50 |
|
16 |
00Cr18Ni14Mo2Cu2 |
≤0.03( |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00-16.00 |
17.00-19.00 |
1.20-2.75 |
|
Cu1.00-2.50 |
|
17 |
1Crl8Ni9Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-11.00 |
17.00-19.00 |
|
5(wc-0.02)
-0.08 |
|
|
鐵素體型 |
18 |
0Cr13 |
≤0.08 |
≤0.60 |
≤0.80 |
≤0.035 |
≤0.030 |
① |
12.00-14.00 |
|
|
|
|
奧氏體-鐵
索體型 |
19 |
0Cr26Ni5Mo2 |
≤0.08 |
≤1.00 |
≤1.50 |
≤0.035 |
≤0.030 |
3.00-6.00 |
23.00-28.00 |
1.00-3.00 |
|
|
| 